Tipo | Composición química | |||||||||
AWSA5.1 | AWS A5.1M | C | Minnesota | Si | P | S | Ni | Cr | Mes | V |
E6011 E6013 | E4311 E4313 | ≤0.20 | ≤1.20 | ≤1.00 | ... | ... | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
E7016 E7018 | E4916 E4918 | ≤0.15 | ≤1,60 | ≤0.75 | ≤0.035 | ≤0.035 | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
E7018M | E4918M | ≤0.12 | 0,40~1,60 | ≤0.80 | ≤0.030 | ≤0.020 | ≤0.25 | ≤0.15 | ≤0.35 | ≤0.05 |
E308-16 E308L-16 | E308-17 E308L-17 | ≤0.08 | 0,50~2,50 | ≤1.00 | ≤0.04 | ≤0.03 | 9,0~11,0 | 18,0~21,0 | ≤0.75 | Cu ≤ 0,75 |
≤0.04 | ||||||||||
E309 -16 E309L-16 | E309-17 E316-17 | ≤0.15 | 0,50~2,50 | ≤1.00 | ≤0.04 | ≤0.03 | 12,0~14,0 | 22,0~25,0 | ≤0.75 | Cu ≤ 0,75 |
≤0.04 | ||||||||||
E316-16 E316-16 | E316L-17 E309L-17 | ≤0.08 | 0,50~2,50 | ≤1.00 | ≤0.04 | ≤0.03 | 11,0~14,0 | 17,0~20,0 | 2.0~3.0 | Cu ≤ 0,75 |
≤0.04 | ||||||||||
E312-16 | E312-17 | ≤0.15 | 0,50~2,50 | ≤1.00 | ≤0.04 | ≤0.03 | 8,0~10,5 | 28,0~32,0 | ≤0.75 | Cu ≤ 0,75 |
Nota: componentes E7016 y E7018 de Mn+Ni+Cr+Mo+VS1.75; código de electrodo de acero inoxidable interpretación - ejemplo E308-XX (E308-15/E308-16/E308-17/E308-26…...), el código de prefijo se divide en -1/-2/-4, representando la posición de soldadura;el código de sufijo se divide en -5l-6/-7, en el que 5 representa la alcalinidad, 6 representa el rutilo y 7 representa el tipo de ácido titánico. |
Tipo | Propiedades mecánicas | ||||||
AWSA5.1 | AWS A5.1M | Resistencia a la tracción MPa | Límite elástico Mpa | Elongación A (%) | Valor de impacto | gráficos de radio | |
KV2(J) -45℃ | KV2 ()-30 ℃ | ||||||
E6011 | E4311 | ≥430 | ≥330 | ≥22 | ... | ≥ 27 | Grado II |
E6013 | E4313 | ≥430 | ≥330 | ≥17 | ... | ... | |
E7016 | E4916 | ≥490 | ≥400 | ≥22 | ≥ 27 | ≥ 27 | Grado I |
E7018 | E4918 | ≥490 | ≥400 | ≥22 | ≥ 27 | ≥ 27 | |
E7018M | E4918M | Normales ≥ 490 | 370~500 | ≥24 | ... | ≥ 67 | |
2,4 mm/370~530 | |||||||
E308-XX | ≥550 | ≥30 | |||||
E308L-XX | ≥520 | ||||||
E309-XX | ≥550 | ||||||
E309L-XX | ≥520 | ||||||
E316-XX | ≥520 | ||||||
E316L-XX | ≥490 | ||||||
E312-XX | ≥ 660 | ≥22 | |||||
Nota: E6011 no tiene requisitos especiales para el horno de conservación del calor y la drvina: Temperatura ambiental: 20 ~ 40 C; El requisito del horno de conservación del calor E6013 es más alto que la temperatura ambiente [10 C ~ 20 C]; El secado requiere secar al menos 1 hora a 120 C150 C;Requisitos E7016/E7018/E7018M para hornos de conservación de calor y secado;Temperatura ambiental: [30C~140C]; El secado requiere secado por lo menos 1~2 horas a 260℃~425℃; |
milímetro: 0,8 mm / 0,9 mm / 1,0 mm / 1,2 mm / 1,6 mm
pulgada: 0,030 / 0,035 / 0,040 / 0,045/ 3/16 - 3/64
milímetro: 1,2 mm/ 1,6 mm/ 2,0 mm/ 2,4 mm/ 3,2 mm/ 4,0 mm